ГОСТ CДП1-2 Enquiry | Print this page
ГОСТ CДП1-2 Details
CДП1-2
ГОСТ CДП1-2 Standard Download
| Category | Type | Grade | Designations |
|---|---|---|---|
| Grades | Special Alloy | CДП1-2 | Russia - ГОСТ , |
Chemical composition % of the ladle analysis of grade CДП1-2
| C(％) | Si(％) | Cr(％) | Ni(％) | Cu(%) | Al(%) | Other(%) |
|---|---|---|---|---|---|---|
| Max 0.05 | Max 0.2 | 18-22.00 | Balance | Max 0.05 | 11-13.500 | 0、N、H:Total: 0.02 |
| Proof strength Rp0.2 (MPa) |
Tensile strength Rm (MPa) |
Impact energy KV (J) |
Elongation at fracture A (%) |
Reduction in cross section on fracture Z (%) |
As-Heat-Treated Condition | Brinell hardness (HBW) |
|---|---|---|---|---|---|---|
| 467 (≥) | 586 (≥) | 42 | 31 | 32 | Solution and Aging, Annealing, Ausaging, Q+T,etc | 321 |
| Property | Density kg/dm3 |
Temperature T °C/F |
Specific heat J / kgK |
Thermal conductivity W/mK |
Electric resistance µΩ·cm |
Modulus of elasticity kN/mm2 |
Expansion rate |
|---|---|---|---|---|---|---|---|
| 122 (≥) | 194 (≥) | 23 | 12 | 33 | Solution and Aging, Annealing, Ausaging, Q+T,etc | 431 | |
| Temp. °C/°F |
Creep strain limit (10000h) (Rp1,0) N/mm2 |
Creep rupture strength (10000h) (Rp1,0) N/mm2 |
|||||
| 957 | 923 | 456 |
| Product type | Products | Dimension | Processes | Deliver Status |
|---|---|---|---|---|
| Plates / Sheets | Plates / Sheets | 0.08-200mm(T)*W*L | Forging, hot rolling and cold rolling | Annealed, Solution and Aging, Q+T, ACID-WASHED, Shot Blasting |
| Steel Bar | Round Bar, Flat Bar, Square Bar | Φ8-1200mm*L | Forging, hot rolling and cold rolling, Cast | Black, Rough Turning, Shot Blasting, |
| Coil / Strip | Steel Coil /Steel Strip | 0.03-16.0x1200mm | Cold-Rolled & Hot-Rolled | Annealed, Solution and Aging, Q+T, ACID-WASHED, Shot Blasting |
| Pipes / Tubes | Seamless Pipes/Tubes, Welded Pipes/Tubes | OD:6-219mm x WT:0.5-20.0mm | Hot extrusion, Cold Drawn, Welded | Annealed, Solution and Aging, Q+T, ACID-WASHED |
| Grade | Standard | Country | Application |
|---|---|---|---|
| CДП1-2 | Russia TY standard high temperature oxidation the chemical composition of casting alloy rod |